Abstract
Highly cis-1,4 selective (up to 98%) coordination-insertion polymerization of 1,3-butadiene (BD) has been achieved herein using acenaphthene-based α-diimine cobalt complexes. Due to the presence of intra-ligand π-π stacking interactions, the complexes revealed high thermostability, affording polybutadiene products in high yields. Moreover, all of the obtained polymers possessed a relatively narrow molecular weight distribution as well as high molecular weight (up to 92.2 × 10(4) Dalton). The molecular weights of the resultant polybutadienes could be finely tuned by varying polymerization parameters, including temperature, Al/Co ratio, etc. Moreover, the copolymerization of butadiene with polar monomer 2-(4-methoxyphenyl)-1,3-butadiene (2-MOPB) was also successfully realized to produce a type of polar cis-1,4 polybutadiene (cis-1,4 content: up to 98.1%) with a range of 2-MOPB content (0.46-1.83%). Water contact angle measurements indicated that the insertion of a polar monomer into a polymer chain could significantly improve the polymer's surface property.