Abstract
The synthesis of environmentally friendly antimicrobial polymeric coatings, especially in the case of aquaculture, that inhibit the growth of bio-deposits is a very important issue that will contribute to the cost reduction of nets' cleaning process as well as the protection of the submarine wealth from the biostatic substances used so far. In the present work, the antimicrobial polymers P(SSAmC(16)-co-VBCHAMx) and the terpolymer P(SSAmC(16)w-co-VBCHAMx-co-GMAy) were synthesized, bearing quaternary ammonium compounds, electrostatically bound and covalently attached at the same polymer chain. The combination of the two types is of particular importance, as it can provide effective antimicrobial polymeric materials with self-polishing capabilities as a result of the released nature of the antimicrobial, in combination with the permanent local action of the immobilized species. The cross-linking reaction of the terpolymer P(SSAmC(16)w-co-VBCHAMx-co-GMAy) with the homopolymer polyacrylic acid (PAA) was tested at 120 °C in terms of the equivalent ratio between epoxy and carboxyl groups. The synthesized polymers were further used for the coating of aquaculture nets and tested in terms of antifouling efficiency in lab and scale-up conditions. Uncoated nets were also used in all applications for comparison reasons. The coated nets performed efficiently for 35 days in lab-scale and 66 days in scale-up conditions, showing a high antifouling activity in both fields compared to the uncoated nets.