Abstract
This study investigates the combined influence of superabsorbent polymers (SAPs) with distinct absorption kinetics and extended mixing sequences on the rheological, mechanical, and transport properties of high-performance concrete (HPC). Two SAPs-an ionic acrylamide-co-acrylic acid copolymer (SAP-P) and a non-ionic acrylamide polymer (SAP-B)-were incorporated at an internal curing level of 100%. The impact of extended mixing times (3, 5, and 7 min) following SAP addition was systematically evaluated. Results showed that longer mixing durations led to increased superplasticizer demand and higher plastic viscosity due to continued water absorption by SAPs. However, yield stress remained relatively stable owing to the dispersing effect of the added superplasticizer. Both SAPs significantly enhanced the static yield stress and improved fresh stability, as evidenced by reduced surface settlement. Despite the rheological changes, mechanical properties-including compressive and flexural strengths and modulus of elasticity-were consistently improved, regardless of mixing duration. SAP incorporation also led to notable reductions in autogenous and drying shrinkage, as well as enhanced electrical resistivity, indicating better durability performance. These findings suggest that a 3 min extended mixing time is sufficient for effective SAP dispersion without compromising performance.