Abstract
The production of wheat straw waste board materials encounters challenges, including inadequate inherent adhesiveness and the utilization of environmentally harmful adhesives. Employing a hot-pressed method for converting wheat straw into board materials represents a positive stride towards the resourceful utilization of agricultural wastes. This study primarily focuses on examining the influence of hot-pressing process conditions on the mechanical properties of wheat straw board materials pretreated with dilute acid. Additionally, it assesses the necessity of dilute acid treatment and optimizes the hot-pressing conditions to achieve optimal results at 15 MPa, 2 h, and 160 °C. Furthermore, a comprehensive process is developed for preparing wheat straw hot-pressed board materials by combining dilute acid pretreatment with surface modification treatments, such as glutaraldehyde, citric acid, and rosin. Finally, a thorough characterization of the mechanical properties of the prepared board materials is conducted. The results indicate a substantial improvement in tensile strength across all modified wheat straw board materials compared to untreated ones. Notably, boards treated with glutaraldehyde exhibited the most significant enhancement, achieving a tensile strength of 463 kPa, bending strength of 833 kPa, and a water absorption rate of 14.14%. This study demonstrates that combining dilute acid pretreatment with surface modification treatments effectively enhances the performance of wheat straw board materials, offering a sustainable alternative to traditional wood-based board materials.