Abstract
Ceramics are considered to be candidate materials for galvanising pot bearing materials due to their excellent corrosion resistance in many molten metals. Galvanising pot roll bearings must have excellent wear resistance, and, therefore, it is important to understand the wear behaviour of prospective bearing materials. This study investigates the friction- and wear-resistant properties of select ceramics, namely, pure hBN, BN M26, AlN-BN, Macor, 3YSZ, Al(2)O(3) and Si(3)N(4). The ceramics were tested at different sliding speeds using a pin-on-disc device equipped with SiC pins. The lowest coefficient of friction (COF) achieved was below 0.1, and it was measured for pure hBN at a 3.14 m/min sliding speed. However, a wear scar analysis showed that the BN grades suffered from severe wear. The highest wear rate was obtained for BN M26 at a 9.42 m/min sliding speed and was equal to 17.1 × 10(-6) mm(3) N(-1) m(-1). It was shown that the wear coefficient of the tested ceramics varied exponentially with hardness. The lowest wear was observed on the 3YSZ, Al(2)O(3) and Si(3)N(4) ceramics, which showed no volume loss, and, for this reason, they can be potentially used as bearing materials in continuous galvanising lines.