Abstract
OBJECTIVES: The aim of the study was to analyze the occurrence of stress on teeth with abfraction lesions restored with six different restorative materials, and by introducing the tensile strength parameters to calculate the safety factor of the material under the load (ratio between the strength of the material and the maximum stress). MATERIALS AND METHODS: Three-dimensional models of the mandibular premolar are created from a microcomputed tomography images. An abfraction lesion is modeled on the tooth. The stress of the dental tissues and six restorative materials under functional and nonfunctional occlusal loading of 200 (N) are analyzed by finite element method. STATISTICAL ANALYSIS: CTAn program 1.10 and ANSYS Workbench (version 14.0) were used for analysis. Results are presented in von Mises stress. RESULTS: Oblique loads caused ≈ four times higher stress in restorative materials than the axial ones. It is noticeable that high values of von Mises stress are measured at the bottom of the sharp lesion, even up to 240 MPa, that are significantly reduced after the restoration. The highest stresses at the restorative material are present at the lower (gingival) margin of the restoration. The highest stresses under both types of loads are measured in nanohybrid composite (Tetric EvoCeram, Ivoclar Vivadent). The lowest values of the stress are measured in the flowable composite (Tetric Flow, Ivoclar Vivadent), but at the same time, the highest value of the stress is measured in the surrounding dental tissues on the tooth restored with the flowable composite. The microhybrid composite (Herculite XR, Kerr), with the highest safety factor, is the material that best withstands the stresses it is exposed to. The obtained safety factor did not exceed the critical limit, except for the glass ionomer cement, with the safety factor lower than 1. CONCLUSION: The type of tooth loading has the greatest influence on the intensity of stress. The value of the obtained stresses in the restorative material and dental tissues differ due to the different mechanical properties of the materials. Restoration of noncarious lesions significantly reduces extremely high stress values at their bottom.