Abstract
Presence of microcracks in concrete can diminish the service life of a structure. The injection of materials for filling the crack is proposed for facing this problem. The traditional materials used for sealing cracks present some drawbacks, such as the difficulties of inorganic materials for flowing to all the depth of the crack and the lack of compatibility with the cementitious matrix in the case of organic materials. In this work, the injection of colloidal nanosilica dispersed in water is proposed for filling microcracks in mortars. The effect of the injection procedure on the sealing performance of the colloidal nanosilica has been assessed. The ability of colloidal nanosilica for penetrating through the crack and its posterior gelification-solidification inside the crack after a curing period have been confirmed. The microscopic analysis of a cross-section of the crack indicates that the sealing ability of the nanosilica seems to be not only due to the filling of the crack but also to chemical interactions with the cementitious phases of the surrounding crack sides.