Abstract
PURPOSE: In the authors' experience, the color of silicone elastomer following polymerization in molds made of gypsum products is slightly different from the color that was matched in the presence of the patient, before the silicone is packed. It is hypothesized that the investing materials and separating media have an effect on the color during the polymerization process of the silicone. MATERIALS AND METHODS: This study compares and evaluates the change in color of silicone elastomer packed in three commonly used investing materials - Dental stone (white color), dental stone (green color), and die stone (orange color); coated with three different separating media - Alginate-based medium, soap solution and a resin-based die hardening material. Pigmented silicone samples of dimensions 1.5 cm × 2 cm × 0.5 cm were made from the elastomer in the above-mentioned mold materials using combinations of the mentioned separating media. These served as test group samples. Control group samples were made by packing a mix of the same pigmented elastomer in stainless steel molds. The L*, a*, b* values of the test and control group samples were determined using a spectrophotometer. The change in color (Delta E) was calculated between the control and test groups. RESULTS: The mean L, a, b values for the control group were, 31.8, 26.2, and 36.3, respectively. Average values of change in color (Delta E) for samples packed utilizing alginate-based medium, die hardener, and soap solution, respectively in white dental stone (2.70, 2.74, and 2.88), green dental stone (2.19, 2.23, 2.42), and orange die stone (3.19, 2.72, 2.80) were tabulated. CONCLUSION: Among the investing materials studied, die stone showed the most color change (3.19), which was statistically significant. Among the separating media, die hardener showed the least color change (2.23). The best combination of an investing material and separating media as per this investigation is a dental stone (green) and alginate-based separating medium.