Abstract
This study investigates the recovery of uranium(vi) using a novel functionalized polyglycidyl methacrylate (PGMA) adsorbent, PPA-PGMA, modified with polyamine-phosphonic acid. The adsorbent's structure was confirmed by CHNP, BET, SEM, TGA, XRD, XPS, and FTIR analyses. Batch adsorption studies from synthetic solutions revealed an optimal pH range of 3.0-6.0, where the saturation adsorption capacity reached 0.828 mmol g(-1). The adsorption process exhibited fast kinetics (180 min) and was endothermic. Experimental data fitted well with the Langmuir and pseudo-second-order (PSO) kinetic models. The adsorption process was quantitatively described using a new three-dimensional (3D) nonlinear mathematical model, which was verified using MATLAB software against several theoretical models (generalized Langmuir, PSO with Arrhenius, shrinking core, and Floatotherm models). Thermodynamic analysis indicated a spontaneous (ΔG < 0) and endothermic (ΔH > 0) reaction. The adsorbent demonstrated excellent reusability, maintaining high efficiency over six cycles. Metal desorption was successfully achieved using NaHCO(3), with adsorption capacity remaining at 88-90% of the initial value after the sixth cycle. Finally, PPA-PGMA was applied to recover U(vi) from acidic ore leachates (El-Sella and Gattar areas) following precipitation pre-treatment. The adsorbent exhibited marked selectivity for U(vi) over co-existing Fe and Si, achieving adsorption capacities of 0.71 mmol U per g (El-Sella) and 0.65 mmol U per g (Gattar). These results confirm the potential of PPA-PGMA as a durable and selective adsorbent for uranium recovery from complex acidic matrices.