Abstract
Elevated phosphorus levels in wastewater created significant environmental concerns, including the degradation of surrounding soil structure, inhibition of plant growth, and potential threats to human health. To address this issue, a self-standing nanofibrous composite membrane based on PA-66/PVA-15%La(OH)(3) was fabricated via electrospinning, followed by glutaraldehyde (GA) crosslinking and alkali hydrolysis to create an interpenetrating structure, where PA-66 provided the overall mechanical strength of the membrane, while La served as a functional component for the adsorption of phosphate. The chemical composition, surface morphology, thermal stability, and mechanical properties of the resulting membranes were characterized using ATR-FTIR, SEM, TGA, and tensile testing, respectively. Furthermore, the adsorption performance of the membranes was evaluated systematically through static and dynamic adsorption. The Langmuir isotherm model yielded a theoretical maximum adsorption capacity of 21.39 mg/g for phosphate ions. Notably, over 96% of this capacity was retained even in the presence of interfering ions. Moreover, dynamic adsorption experiments demonstrated that the membrane can deal with 1.74 L of phosphate-containing wastewater at a low flow rate of 1.0 mL/min and 1.46 L at a high flow rate of 2.0 mL/min, respectively, while consistently maintaining a phosphate removal efficiency exceeding 90%. A controlled release of phosphate ions from a phosphate-adsorbed membrane was successfully demonstrated using Mougeotia cultivation, implying the potential for phosphorus resource recovery.