Abstract
2-Pyrone-4,6-dicarboxylic acid (PDC) is a chemically stable metabolic intermediate of lignin that can be produced on a large scale by transforming bacteria. Novel biomass-based polymers based on PDC were synthesized by Cu(I)-catalyzed azide-alkyne cycloaddition (CuAAC) and fully characterized by nuclear magnetic resonance, infrared spectroscopies, thermal analysis, and tensile lap shear strength measurements. The onset decomposition temperatures of these PDC-based polymers were all above 200 °C. In addition, the PDC-based polymers exhibited strong adhesive properties to various metal plates, with the highest adhesion to a copper plate of 5.73 MPa. Interestingly, this result was in contrast to our previous findings that PDC-based polymers weakly adhere to copper. Furthermore, when bifunctional alkyne and azide monomers were polymerized in situ under hot-press conditions for 1 h, the resulting PDC-based polymer displayed a similar adhesion to a copper plate of 4.18 MPa. The high affinity of the triazole ring to copper ions improved the adhesive ability and selectivity of the PDC-based polymers to copper while still maintaining the strong adhesive ability to other metals, which is conducive to enhancing the versatility of PDC-based polymers as adhesives.