Abstract
In situ high pressure and high temperature (HPHT) study has been carried out on C(60)/ferrocene (Fc) in order to detect the process of polymerization and reveal the polymerization mechanism. Pristine C(60) was also studied under same conditions for comparison. In both cases, similar types of polymers can be observed after pressure and temperature release, but with different fractions, i.e. a larger amount of 2D polymers were formed in pure C(60), while more branch-like polymers were synthesized in C(60)/Fc, although the most fraction of the polymers is still 1D chain-like polymer in both of the materials. The polymers formed in C(60) can be detected both during the "up" run (pressure and temperature increase) and the "down" run (pressure and temperature decrease), while in C(60)/Fc, the polymers can only be synthesized in the "down" run. The differences between the two cases were attributed to the different initial lattice structures of the two materials and the confinement effect of the dopant. The polymerization mechanism on C(60)/Fc under HPHT was also revealed in this work.