Abstract
In this paper, Ni60/WC wear-resistant coatings have been created on the Ti6Al4V substrate surface using a pre-layered powder laser cladding method by deploying various scanning speeds of 8, 10, 12, and 14 mm/s. The coatings are characterized through X-ray diffraction (XRD), scanning electron microscopy (SEM), and a high-speed reciprocating fatigue wear tester. It is found that the phase composition of the coating comprises the synthesized, hard phase TiC and TiB(2), the silicides WSi(2) and W5Si(3), and NiTi and γ-Ni solid solutions. At different scanning speeds, there is a metallurgical fusion line in the bonding area of the fused cladding layer, indicating a good metallurgical bonding between the substrate and the powder. At a low scanning speed, the coating develops into coarse dendrites, which shows significant improvement with scanning speed. The microhardness first increases and then decreases with the scanning speed, and the coating's average microhardness was 2.75-3.13 times higher than that of the substrate. The amount of mass wear has been reduced by 60.1-79.7% compared to the substrate. The wear behavior of the coatings was studied through detailed analysis of wear surfaces' microstructures and the amount of wear to identify the optimum scanning speed.