Abstract
Decapod crustaceans have tooth-like white denticles that are present only on the pinching side of the claws. In the mud crab, Scylla serrata, a huge denticle exists on the movable finger of the dominant claw. This is mainly used to crush the shells of the crab's staple food. The local mechanical properties, hardness (H(IT)) and elastic modulus (E(r)), of the peak and valley areas of the largest denticle were examined via a nanoindentation test. The microstructure and elemental composition were characterized using a scanning electron microscope and energy-dispersive X-ray spectroscopy. The striation patterns originating from a twisted plywood structure parallel to the surface were visible over the entire denticle. Most of the largest denticle was occupied by a hard area without phosphorus, and there was a soft layer corresponding to the endocuticle with phosphorus in the innermost part. The H(IT) of the denticle valley was about 40% lower than that of the denticle peak, and the thickness of the soft endocuticle of the denticle valley was five times thicker than that of the denticle peak. The H(IT)-E(r) map showed that the abrasion resistance of the denticle surface was vastly superior and was in the top class among organisms. The claw denticles were designed with the necessary characteristics in the necessary places, as related to the ecology of the mud crab.