Abstract
This study aims to evaluate the changes of fragility and ultrastructure of amniotic membrane after cross-linking by UVA/riboflavin.Forty-nine fresh amniotic membranes were randomly divided into 3 groups. Eighteen were in group A (CX group) and immersed in 0.1% riboflavin solution for 10 min for UVA/riboflavin cross-linking. Sixteen were in group B (B2 group), soaked for 10 min with 0.1% riboflavin. After soaking, membranes in group A and B were transferred into corneal preservation solution. Fifteen pieces were in group C, directly into corneal preservation solution. The biomechanical and ultrastructural changes of the amniotic tissue before and after cross-linking were examined (CX group = 13, B2 group = 11, C group = 15). The amniotic membrane tissue of group A (n = 5) and B (n = 5) was transplanted into 16 eyes of the rabbits, respectively, and the dissolution time of the amniotic membrane tissue was investigated.After cross-linking, compared with the control group, the elastic modulus of the low-stress area of the amniotic membrane (Elow) was higher, while the elastic modulus of the high-stress area of the amniotic membrane (Ehigh) was lower, with no significant difference in the tensile strength. Also, the collagen fibers showed coarse and bamboo-like changes. In group A, amniotic membranes began to dissolve 4 weeks after conjunctiva transplantation, and all amniotic membranes were dissolved and absorbed 6 weeks after conjunctiva transplantation. In group B, some amniotic membrane tissues were still visible 6 weeks after conjunctiva transplantation.This study suggested that after amniotic membrane cross-linking, the brittleness was increased, the hardness was enhanced, and the morphology of the collagen fiber was changed. The cross-linked amniotic membrane showed resistance to tissue dissolution.