Abstract
The main challenges facing composite restorations are secondary caries and bulk fracture. The objective of this study was to develop nano DCPA (dicalcium phosphate anhydrous)-whisker composites with high strength and Ca and PO(4) ion release to combat caries. Flexural strength for the nano DCPA-whisker composites at a nano DCPA:whisker mass ratio of 1:2 ranged from (148 +/- 9) MPa to (167 +/- 23) MPa, significantly higher than the (103 +/- 32) MPa of an inlay/onlay commercial control composite without Ca-PO(4) release. The nano DCPA-whisker composite released PO(4) to a concentration of (1.95 +/- 0.13) mmol/L and Ca of (0.68 +/- 0.05) mmol/L. Compared with previous conventional Ca- and PO(4)-releasing composites, the nano DCPA-whisker composites had strengths two-fold higher, and released comparable or higher levels of Ca and PO(4). In conclusion, combining nano-DCPA with whiskers yielded novel composites that released high levels of Ca and PO(4) requisite for remineralization. These high-strength composites may provide a unique combination of stress-bearing and caries-inhibiting capabilities.