Transformation of β-Ni(OH)(2)to NiO nano-sheets via surface nanocrystalline zirconia coating: Shape and size retention

Shape and size of the synthesized NiO nano-sheets were retained during transformation of sheet-like β-Ni(OH)(2)to NiO at elevated temperatures via nano-sized zirconia coating on the surface of β-Ni(OH)(2). The average grain size was 6.42 nm after 600 °C treatment and slightly increased to 10 nm after 1000 °C treatment, showing effective sintering retardation between NiO nano-sheets. The excellent thermal stability revealed potential application at elevated temperatures, especially for high temperature catalysts and solid-state electrochemical devices.