Abstract
Nano-scale crystal defects extremely affect the security and reliability of the explosive charges of weapons. In order to understand the evolution of nano-scale defects of 2,4,6,8,10,12-hexanitro-2,4,6,8,10,12-hexaaza-isowurtzitane (CL-20) explosive crystals under thermal treatments, the specific surface, volume fraction and size distribution of the nano-scale defects were studied by using Wide Angle X-ray Scattering (WAXS) and Small Angle X-ray Scattering (SAXS) during the temperature range from 30 °C to 200 °C. The results showed that the number and size of the pores in CL-20 powder did not change significantly during the heating process before phase transformation (30-160 °C). At 170 °C, CL-20 began to convert from ε- to γ- phase, and the specific surface and volume fraction of the nano-scale defects increased significantly. Further investigation of the pore size distribution showed that the number of pores with a small size (radius 9-21 nm) changed particularly significantly, resulting from the cracking of the CL-20 crystal powder during phase transition. At 200 °C, the phase transition was completed and γ-CL-20 was created, and the small-sized pores gradually grew into medium-sized (radius 21-52 nm) pores over time when the temperature was fixed at 200 °C.