Abstract
Nanocomposites of polyvinylidene fluoride (PVDF) with dimensional (1D) cobalt oxide (Co(3)O(4)) and f-MWCNTs were prepared successfully by the solution casting method. The impact of 1D Co(3)O(4) filler and 1D Co(3)O(4)/f-MWCNTs co-fillers on the structural, thermal, and electrical behavior of PVDF were studied. The crystal structural properties of pure PVDF and its nanocomposite films were studied by XRD, which revealed a significant enhancement of β-phase PVDF in the resulting nanocomposite films. The increase in β-phase was further revealed by the FTIR spectroscopic analysis of the samples. TG, DTA, and DSC analyses confirmed an increase in thermal stability of PVDF with the addition of nano-fillers as well as their increasing wt.%. From impedance spectroscopic studies, it was found that the DC conductivity of PVDF increases insignificantly initially (up to 0.1 wt.% of nano-fillers addition), but a significant improvement in DC conductivity was found at higher concentrations of the nano-fillers. Furthermore, it was observed that the DC conductivity decreases with frequency. The increase in DC conductivity corresponded to the strong interactions of nano-fillers with PVDF polymer chains.