Abstract
BACKGROUND: It is well established that nanotopography and wettability of implant surfaces contribute to osseointegration and long-term implant success. However, the effects of a hydrogenated surface with nanotubular and superhydrophilic properties on peri-implant soft tissue remain unclear. This study was designed to study the impact of a modified abutment surface on early soft tissue integration compared with a machined surface. METHODS: Thirty-six implants were placed at the bone level in the bilateral mandible of six beagles, followed by healing abutments belonging to the standard machined Ti-6Al-4V alloy abutments (TC4-M), anodized abutments with nanotubes (TC4-Nano), and hydrogenated abutments (TC4-H/Nano) groups, which were randomly screwed to the implants. After two and four weeks of wound healing, the animals were euthanized for histological evaluation. RESULTS: A superhydrophilic nanotubular surface developed on the hydrogenated abutment. Histological and histometric analyses revealed similar peri-implant soft tissue healing and dimensions for the three types of abutments at two and four weeks. Connective tissue (CT) length was longer around TC4-H/Nano abutments compared with standard abutments; however, the differences were not statistically significant. Moreover, collagen fibers in the TC4-H/Nano group extended and were attached perpendicularly to the superhydrophilic surface. CONCLUSIONS: Our results revealed that the soft tissue interface adjacent to the hydrogenated abutment is comparable to that of the machined abutment. A tendency of increased CT length and perpendicular collagen fibers was observed around the modified abutment. This study suggests that nanotubular/superhydrophilic surfaces could be a promising modification to enhance soft tissue sealing. However, comprehensive studies should be conducted to evaluate the peri-implant soft tissue around the modified abutment immunohistochemically, histopathologically, and clinically.