Abstract
The effects of temperature and time variances on nano-additives treatment of mild steel during machining was presented in this study. Mild steel of 150 kg mass containing 0.56% carbon was charged into the furnace at melting and pouring temperature of 1539 and 1545 °C respectively. Also charged into the furnace with the mild steel were 0.05% max phosphorous and a bit of sulphur. Thereafter, the sample was cooled and annealed at a temperature of 900 °C for 9 h and then cooled to 300 °C of hardening, normalizing and tempering respectively. The treated samples were then soaked with pulverized in palm kernel shell and barium carbonate (20%) energizer at respective temperatures (800, 850, 900 and 950 °C) and time variances (60, 90 and 120 min) in a muffle furnace. The developed tool was tested on a lathe machine to evaluate its performance. The surface and core hardness, wear resistance and toughness were carried out using the hardness tester, Rotopol-V and impact tester respectively. This is essential for predicting the useful life of the tool in service.