Abstract
Calcium magnesium phosphate cements (CMPCs) were obtained starting from dolomite (alone or mixed with fly ash) thermally treated at two different temperatures. Dolomite calcination at 750 °C for 3 h determined the formation of a mixture of MgO and CaCO(3). The mixing of dolomite with fly ash and the increase in the calcination temperature at 1200 °C determined the formation of new compounds (calcium aluminum silicate and calcium magnesium silicates), which are present along with MgO and small amounts of CaO in the thermally treated material. These two precursors were mixed with KH(2)PO(4) solution and borax (as a retardant admixture) to obtain the CMPCs. The setting time and compressive strengths of these CMPCs were assessed and the XRD analyses provided insights into their mineralogical composition after hardening and thermal treatment. The cements, as so or mixed with perlite, were applied on steel plates, to assess their behavior when put in direct contact with a flame. The compatibility of these materials with the steel substrate was evaluated by scanning electron microscopy (SEM). The direct contact with the flame up to 60 min provided information regarding the CMPCs' ability to prevent the rapid increase in the substrate (steel plate) temperature. The findings indicate that CMPC pastes and composites containing perlite can offer a degree of protection for steel structures in the event of a fire.