Abstract
Liquid accelerating agents have the advantages of simple operation and fast construction, and have become indispensable admixtures in shotcrete. However, most liquid accelerating agents in the market at present contain alkali or fluorine, which adversely affect concrete and seriously threaten the physical and mental health of workers. Therefore, in view of the above deficiencies, it is necessary to develop a new type of alkali-free fluorine-free liquid accelerating agent. In this paper, the polyaluminum sulfate early strength alkali-free liquid accelerator is prepared using polymeric aluminum sulfate, diethanolamine, magnesium sulfate heptahydrate and nano-silica. The influence of this agent on the setting time of fresh cement paste and compressive strength of the corresponding cement mortar is determined. Thermogravimetric analysis curves, X-ray diffraction and scanning electron microscopy images are obtained to investigate the mechanism. Findings show that the initial setting time and the final setting time of cement paste are 2 min 30 s and 7 min 25 s. The compressive strengths of cement mortar cured for 1 d, 28 d and 90 d are 2.4 MPa, 52.2 MPa and 54.3 MPa respectively. Additionally, the corresponding flexural strengths are 3.4 MPa, 9.8 MPa, 11.8 MPa. When the mass rate of accelerator is 7%, the mechanical strengths of cement mortar are the highest. The additions of fly ash and blast furnace slag can affect the mechanical of cement mortar mixed with accelerator. When the mass ratio of the fly ash and blast furnace slag is 15%, the mechanical strengths of cement mortar reach the highest. Moreover, the hydration heat release rate of cement is increased by the accelerator and the corresponding time of hydration heat peak is decreased by the accelerator. The accelerator can decrease the amount of needle-like hydration products and improve the compactness. The mechanical strengths are improved by consuming a large amount of Ca(OH)(2) and forming more compact hydration products. It is recommended that the optimum dosage range of the polyaluminum sulfate early strength alkali-free liquid accelerator is 7%.