Abstract
Silica fly ash, Certyd aggregate, and an alkaline solution were used to produce lightweight geopolymer concretes. The compressive strength, water absorption, and bulk density results, along with SEM photos showing the structure of the obtained composite, were obtained. Tests conducted on the specifications of lightweight geopolymer concretes have revealed significant chemical interactions between the ash aggregate and the geopolymer mortar, particularly when the coarse aggregate surface has been pre-treated with an alkaline solution. A statistical analysis of the experimental data, which investigated the influence of three key variables on the compressive strength, water absorption, and bulk density of lightweight geopolymer concrete (LBG), identified the following factors as having the most substantial impact: the quantity of alkali used, the curing temperature, and the concentration of alkali in the mixture. The optimal test series exhibited a commendable compressive strength of 20.14 megapascals (MPa), accompanied by a water absorption rate of 14.72%, and a bulk density of 1486.6 kg per cubic meter (kg/m³). These findings underscore the importance of alkali content, curing temperature, and alkali concentration in tailoring the properties of lightweight geopolymer concrete to meet specific performance requirements.