Abstract
Adhesive joints possess a number of advantages over traditional joining methods and are widely used in composite structures. Conventional non-destructive examination techniques do not readily reveal joint degradation before the formation of explicit defects. Embedded fiber Bragg grating (FBG) sensors and the resistance of carbon nanotube (CNT)-doped conductive joints have been proposed to monitor the structural integrity of adhesive joints. Both techniques will be employed and compared in the current work to monitor damage development in adhesive joints under tensile and cyclic fatigue loading. Most of the previous works took measurements under an applied load, which by itself will affect the monitoring signals without the presence of any damage. Moreover, most FBG works primarily relied on the peak shifting phenomenon for sensing. Degradation of adhesive and inter-facial defects will lead to non-uniform strain that may chirp the FBG spectrum, causing complications in the peak shifting measurement. In view of the above shortfalls, measurements are made at some low and fixed loads to preclude any unwanted effect due to the applied load. The whole FBG spectrum, instead of a single peak, will be used, and a quantitative parameter to describe spectrum changes is proposed for monitoring purposes. The extent of damage is revealed by a fluorescent penetrant and correlated with the monitoring signals. With these refined techniques, we hope to shed some light on the relative merits and limitations of the two techniques.