Abstract
Microstructures of typical carbon fibers (CFs) from polyacrylonitrile (PAN) and pitch-based precursors were studied using a novel digital twin approach with individual carbon fibers for a local crystal scale model. The transmission electron microscopy (TEM) samples were prepared using a focused-ion beam (FIB) for both longitudinal and transverse directions of carbon fibers. Measurements of the crystal size and orientation were estimated from X-ray scattering. TEM imaging of graphitic packing facilitated further comprehension of associations between processing and final material properties, which could enable customization of microstructures for property targets. Then the detailed microstructural information and their X-ray scattering properties were incorporated into the simulation model of an individual carbon fiber. Assuming that graphene properties are the same among different forms of carbon fiber, a reasonable physics-based explanation for such a drastic decrease in strength is the dislocations between the graphitic units. The model reveals critical defects and uncertainty of carbon fiber microstructures, including skin/core alignment differences and propagating fracture before ultimate failure. The models are the first to quantify microstructures at the crystal scale with micromechanics and to estimate tensile and compressive mechanical properties of carbon fiber materials, as well as potentially develop new fundamental understandings for tailoring carbon fiber and composites properties.