Abstract
The effect of high temperature exposure on the water wetting properties of co-electrodeposited superhydrophobic nickel-polytetrafluoroethylene (Ni-PTFE) nanocomposite coating on copper substrates was studied. This was accomplished by comparing the performance with a commercial superhydrophobic spray treatment (CSHST). The Ni-PTFE and CSHST coatings were both subjected to heating at temperatures up to 400 °C. Results showed that the Ni-PTFE was able to maintain its superhydrophobicity throughout the entire temperature range, whereas the CSHST became more wettable at 300 °C. Furthermore, additional abrasive wear tests were conducted on both materials that were subjected to heating at 400 °C. The Ni-PTFE remained highly non-wettable even after 60 m of abrasion length on 800 grit silicon carbide paper, whereas the CSHST coating was hydrophilic after 15 m.