Abstract
Biofilms induce microbial-mediated surface roughening and deterioration of cement. In this study, zwitterionic derivatives (ZD) of sulfobetaine methacrylate (SBMA) and 2-methacryloyloxyethyl phosphorylcholine, were added in concentrations of 0, 1, and 3% to three different types of commercially available resin-modified glass ionomer cement (RMGIC) (RMC-I: RelyX Luting 2, RMC-II: Nexus RMGI, and RMC-III: GC FujiCEM 2). The unmodified RMGICs served as the control group for comparison. The resistance of Streptococcus mutans to ZD-modified RMGIC was evaluated with a monoculture biofilm assay. The following physical properties of the ZD-modified RMGIC were assessed: wettability, film thickness, flexural strength, elastic modulus, shear bond strength, and failure mode. The ZD-modified RMGIC significantly inhibited biofilm formation, with at least a 30% reduction compared to the control group. The addition of ZD improved the wettability of RMGIC; however, only 3% of the SBMA group was statistically different (P < 0.05). The film thickness increased in proportion to the increasing ZD concentrations; there was no statistical difference within the RMC-I (P > 0.05). The experimental groups' flexural strength, elastic modulus, and shear bond strength showed an insignificant decrease from the control group; there was no statistical difference within the RMC-I (P > 0.05). The mode of failure differed slightly in each group, but all groups showed dominance in the adhesive and mixed failure. Thus, the addition of 1 wt.% ZD in RMGIC favorably enhanced the resistance to Streptococcus mutans without any tangible loss in flexural and shear bond strength.