Abstract
BACKGROUND: Since their introduction, there has been limited research regarding the mechanical properties of novel strength-gradient monolithic zirconia. In addition to that, studies evaluating the effect of different core-build materials on the strength of indirect restorations are scarce. Therefore, the aim of this study was to investigate the effect of using different core build-up materials on biaxial flexural strength of a new monolithic multilayered zirconia material. METHODS: Forty zirconia discs were fabricated from IPS e.max ZirCAD Prime (Ivoclar Vivadent AG, Schaan, Liechtenstein) and divided into 2 groups (n = 20). Forty composite discs were prepared from Tetric N-Ceram (Ivoclar Vivadent AG, Schaan, Liechtenstein) and MultiCore Flow (Ivoclar Vivadent AG, Schaan, Liechtenstein). The zirconia discs were adhesively cemented to the 2 types of composite forming 2 groups (Zirconia-Tetric N-Ceram and Zirconia-MultiCore Flow). Biaxial flexural strength was determined using a piston-on-3-ball test. The data were statistically analyzed with an independent t-test for significant differences (p = 0.05). RESULTS: Tetric N-Ceram had significantly higher strength than MultiCore Flow (p < 0.001) but no statistically significant differences were found in strength values between Zirconia-Tetric N-Ceram and Zirconia-MultiCore Flow bilayered samples (p = 0.27). CONCLUSIONS: It was concluded that although the tested composite core materials significantly differ in their biaxial flexural strength values, they had no influence on the biaxial flexural strength of the overlying zirconia.