Abstract
BACKGROUND: Intrafibrillar remineralization within the hybrid layers (HLs) has recently attracted extensive attention in achieving durable resin-dentin bonds. The polyhydroxy-terminated poly(amidoamine) dendrimer (PAMAM-OH) at fourth generation becomes a desirable candidate to induce intrafibrillar remineralization to protect exposed collagen fibrils within HLs based on the size exclusion effect of fibrillar collagen. However, the remineralization process in vivo is time-consuming, during which the exposed collagen fibrils are vulnerable to enzymatic degradation, resulting in unsatisfactory remineralization. Thereby, if PAMAM-OH itself possesses concomitant anti-proteolytic activity during the induction of remineralization, it would be very beneficial to obtain satisfactory remineralization. METHODS: Binding capacity tests using adsorption isotherm and confocal laser scanning microscopy (CLSM) were performed to assess if the PAMAM-OH had adsorption capacity on dentin. Anti-proteolytic testings were detected by MMPs assay kit, in-situ zymography and ICTP assay. Adhesive infiltration of resin-dentin interface and tensile bond strength before and after thermomechanical cycling were implemented to assess if the PAMAM-OH adversely affected resin-dentin bonds. RESULTS: Anti-proteolytic testings performed using MMPs assay kit, in-situ zymography and ICTP assay indicated that PAMAM-OH inhibited exogenous soluble MMP-9 as well as had inhibitory effect on the endogenous proteases. Adhesive infiltration of resin-dentin interface and tensile bond strength before and after thermomechanical cycling were implemented to indicate that the PAMAM-OH pretreatment had no adverse effects on immediate dentin bonding and prolonged the durability of resin-dentin bonds. CONCLUSIONS: PAMAM-OH possesses anti-proteolytic activity and prevents exposed collagen fibrils within HLs from degradation, which lays the foundation for the satisfactory intrafibrillar remineralization induced by PAMAM-OH within HLs to achieve durable resin-dentin bonds in the next work.