Abstract
BACKGROUND: The present study aimed to make a comparison between the effects of 35% hydrogen peroxide gel (HP) and sodium perborate with distilled water (SP) bleaching agents on the sealing characteristics of glass ionomer cement (GIC), TheraBase, ProRoot MTA and Biodentine intraorifice barriers. METHODS: One hundred and twelve single-rooted mandibular human premolar teeth extracted from young patients (14-25 years) were chosen. Root cement and cementoenamel junction (CEJ) of teeth were examined under a stereomicroscope at 10 × magnification to ensure there was no cement defect or dentin gap in CEJ. After the endodontic access cavities were opened on the occlusal surfaces of the teeth, the working length was determined. Instrumentation of each root canal was performed with a ProTaper Gold rotary system in the determined working length and filled with gutta-percha + AH Plus with a single cone technique using. Root fillings were removed 3 mm short of the CEJ and sealed with one of the following intraorifice barrier materials (n = 30/group): 1. GIC; 2. TheraBase; 3. ProProot-MTA; 4. Biodentine. In each of the sub-groups, either HP or SP was used to perform intracoronal bleaching on days 1, 4, and 7. All outer surfaces of the specimens except the 3 mm cervical region were covered with nail polish and modeling wax layers. Specimens were immersed in a 5 ml Eppendorf tube that contained 2 mL of distilled water. The penetration of peroxide release was measured using the colorimetric ferric thiocyanate method. Statistical analysis of the data was performed with Three-way ANOVA and Tukey's test (P = 0.05). RESULTS: In the HP groups, GIC showed the greatest peroxide release when compared with other tested groups on day 1 (P < 0.05). Biodentine and ProRoot MTA displayed a significantly lower peroxide leakage when compared to GIC and TheraBase on days 1 and 4 (P < 0.05). While GIC and TheraBase were used, HP observed higher peroxide penetration when compared with SP on days 1 and 4 (P < 0.05). CONCLUSIONS: Peroxide diffusion was significantly influenced by the kind of intracoronal bleaching agents and intraorifice barrier materials used.