Abstract
Three-dimensional printing is increasingly applied in dentistry to fabricate denture bases. Several 3D-printing technologies and materials are available to fabricate denture bases, but there is data scarcity on the effect of printability, mechanical, and biological properties of the 3D-printed denture base upon fabricating with different vat polymerization techniques. In this study, the NextDent denture base resin was printed with the stereolithography (SLA), digital light processing (DLP), and light-crystal display (LCD) technique and underwent the same post-processing procedure. The mechanical and biological properties of the denture bases were characterized in terms of flexural strength and modulus, fracture toughness, water sorption and solubility, and fungal adhesion. One-way ANOVA and Tukey's post hoc were used to statistically analyze the data. The results showed that the greatest flexural strength was exhibited by the SLA (150.8±7.93 MPa), followed by the DLP and LCD. Water sorption and solubility of the DLP are significantly higher than other groups (31.51±0.92 μgmm3) and 5.32±0.61 μgmm3, respectively. Subsequently, the most fungal adhesion was found in SLA (221.94±65.80 CFU/mL). This study confirmed that the NextDent denture base resin designed for DLP can be printed with different vat polymerization techniques. All of the tested groups met the ISO requirement aside from the water solubility, and the SLA exhibited the greatest mechanical strength.