Abstract
The research on the high-value utilization of biomass has good application prospects and is conducive to sustainable development. In this paper, three different types of activators (potassium hydroxide, phosphoric acid, and polypropylene) were used to carbonize jujube branches at high temperatures of 600 °C and 800 °C, and then the PEG/jujube charcoal composite phase change materials (PCM) were prepared by vacuum impregnation of polyethylene glycol (PEG). The results showed that the carbon support activated by polypropylene (PP) had a richer pore size distribution than the other two activation methods, and the 800 °C carbonization carrier loaded PEG had a higher phase change enthalpy than the composite material at 600 °C. The mesoporous and macroporous structures were staggered with PP-activated jujube charcoal at 800 °C, with a specific surface area of 1082.2 m²/g, the melting enthalpy of the composite material reached 114.92 J/g, and the enthalpy of solidification reached 106.15 J/g after PEG loading. The diffraction peak of the composite phase change material was the superposition of PEG and carbon matrix, which proved that the loading process was physical adsorption. After 200 thermal cycles, the melting enthalpy and crystallization enthalpy were only reduced by 4.3% and 4.1%, respectively, and they remained stable and leak-free at the melting point of PEG for 2 h, demonstrating good thermal stability of the composite phase change materials. In summary, PP has obvious advantages over traditional activation, and the carbon-supported PEG phase change composite after PP activation is a biochar energy storage material with excellent performance.