Abstract
Polyurethane foam compositions derived from bioderived polyester polyols with various additives were evaluated for disintegration under composting conditions using the ISO 20200 standard and were characterized by thermogravimetric analysis, microscopy, infrared spectroscopy, and imaging to provide additional insight. Compared to polyether polyol-based polyurethanes, the bioderived polyurethanes were found to display increased disintegration with an average mass loss of 25.4 ± 3.6 weight percent when subjected to composting conditions for 45 days, suggesting that these materials are less likely to persist in the environment when compared to other types of commodity plastics. Additives such as carbon black and lignin added within the foam composition did not accelerate the disintegration.