Investigation of adhesion status of Candida species to the surface of resin materials produced at different angles with additive manufacturing

The

The surface roughness, contact angle, and adhesion of certain Candida species are affected by printing orientations. Hence, careful consideration of the printing orientation is crucial for fabricating products with desirable properties. In 45-degree production, roughness increases due to the layered production forming steps, whereas in 0-degree production, certain Candida species exhibit high adhesion due to the formation of porous structures. Consequently, considering these factors, it is advisable to opt for production at 90-degrees, while also considering other anticipated characteristics.

Disk-shaped specimens were printed with surgical guide resin using the Liquid Crystal Display production technique in 3 printing orientations (0, 45 and 90-degrees). Surface roughness and contact angle values were evaluated. Real-Time PCR analysis was performed to evaluate Candida adhesion (C. glabrata, C. albicans, C. krusei, C. parapsilosis and C. tropicalis) Field emission scanning electron microscope (FESEM) images of the materials were obtained.

Specimens oriented at 45-degrees demonstrated higher surface roughness (P < .05) and lower contact angle values than other groups. No significant difference was found in the adhesion of C. glabrata, C. albicans, and C. parapsilosis among specimens printed at 0, 45, and 90-degrees orientations (P > .05). A higher proportion of C. krusei and C. tropicalis was found in the specimens printed at orientation degrees of 45 = 90 < 0 with statistical significance. Analyzing the adhesion of all Candida species reveals no statistical disparity among the printing orientations. Conclusions: The surface roughness, contact angle, and adhesion of certain Candida species are affected by printing orientations. Hence, careful consideration of the printing orientation is crucial for fabricating products with desirable properties. In 45-degree production, roughness increases due to the layered production forming steps, whereas in 0-degree production, certain Candida species exhibit high adhesion due to the formation of porous structures. Consequently, considering these factors, it is advisable to opt for production at 90-degrees, while also considering other anticipated characteristics.