Abstract
Hydrogels exhibit exceptional suitability as wound dressing due to their remarkable three-dimensional (3D) characteristics. Here, we have reported the fabrication of hydrogels from biopolymers carboxymethyl cellulose (CMC), polyvinyl alcohol (PVA), and gelatin via a simple blending method to mimic the natural extracellular matrix. Scanning electron microscopy (SEM), water contact meters (WCM), and Fourier-transform infrared spectroscopy (FTIR) were used to evaluate the chemical structural, morphological, and wettability behavior. The wetting and degradation behavior were also found to be different for different formulations (Min. (51.60o) and Max. (113.60o)) and (Min. (38.82 mg) and Max. (3.72 mg)), respectively. Swelling was investigated in different media, including phosphate buffer saline solution (PBS) and aqueous media. It was observed that the hydrogel displayed the highest degree of swelling in an aqueous medium (Min. (597.32-1121.49 %) and Max. (1089.51-2139.73 %)) compared to PBS media (Min. (567.01-1021.85 %) and Max. (899.13-1639.17 %)). The release of Neomycin was studied in a PBS medium via the Franz diffusion method at 37 °C. The maximal release in various media demonstrated pH-responsive behavior. The viability and proliferation of fibroblast (3T3) cell lines were examined in vitro to evaluate cytocompatibility. Human Embryonic Kidney (HEK) 293 cells were used to evaluate the hydrogels' ability to promote vascularization and angiogenesis. Therefore, the data demonstrate that hydrogels that have been manufactured have qualities that make them promising for use as wound dressings in wound healing applications.