Abstract
In the development of ultra-deep wells, extremely high temperatures can lead to inefficiency of additives in drilling fluids. Hence, there is a need to prepare additives with a simple preparation process and good effects at ultra-high temperatures to ensure stable drilling fluid performance. In this study, a high temperature resistant filtration loss polymer (LY-2) was prepared using γ-methacryloyloxypropyltrimethoxysilane (KH570), N,N-dimethylallyl ammonium chloride (DMDAAC), sodium p-styrenesulfonate (SSS), and β-cyclodextrin (β-CD). The impact of the different monomer ratios on particle size, rheology, and filtration performance was systematically investigated. Infrared spectroscopy afforded the structural features. Thermogravimetric Analysis detected the temperature stability, and scanning electron microscopy characterized the polymer micromorphology. LY-2 was completely decomposed at a temperature above 600 °C. Experiments showed FL(API) of the drilling fluid containing 3% LY-2 aged at 260 °C/16 h was only 5.1 mL, which is 85.4% lower compared to the base fluid. This is attributed to the synergistic effect of the polymer adsorption through chemical action at high temperatures and the blocking effect of carbon nanoparticles on the filter cake released by cyclodextrin carbonization at high temperatures. Comparing LY-2 with commercial filter loss reducers shows that LY-2 has excellent temperature resistance, which exhibited five times higher filtration performance and relatively low cost, making it possible to be applied to ultra-high temperature drilling operations in an industrial scale-up.