Abstract
Al-Si-Mg alloys are most commonly used to produce parts by laser powder bed fusion for several industrial applications. A lot of papers have already focused on the effects induced by conventional heat treatments on the microstructure and mechanical properties of AlSi10Mg alloys, rather than on AlSi7Mg. Nobody has investigated thermal stability during long-term direct and artificial aging heat treatments of AlSi7Mg. This study investigates the changes in mechanical properties induced by long-term exposure (512 h) at 150 and 175 °C (the operating temperature of AlSi7Mg) after (i) the laser powder bed fusion process performed on a pre-heated build platform (150 °C), and (ii) heat treatments to the solution at 505 °C per 0.5 and 4 h. Thermal stability was evaluated through both Vickers microhardness measurements to obtain the aging profiles, and tensile tests to evaluate the mechanical properties in specific conditions. An optical microscope was used to investigate the microstructure. It was found that aging at 175 °C confers the same effects induced by a secondary aging heat treatment on as-built samples and, simultaneously, the worst effects on the solution heat treated AlSi7Mg alloy after long-term exposure. The AlSi7Mg DA at both 150 °C and 175 °C showed the same Vickers microhardness (~95 HV0.5), UTS (~300 MPa), and YS (~200 MPa) values for the longest exposure times because the fine and cellular α-Al matrix confers higher stiffness and strength despite the over-aged conditions. On the other hand, the coarsening effects that affected the precipitates during aging at 175 °C, as well as the formation of the precipitate-free zones along the grain boundaries, justified the highest detrimental effects induced on the SHTed samples.