Abstract
Laparoscopes can suffer from fogging and contamination difficulties, resulting in a reduced field of view during surgery. A series of diamond-like carbon films, doped with SiO, were produced by pulsed laser deposition for evaluation as biocompatible, antifogging coatings. DLC films doped with SiO demonstrated hydrophilic properties with water contact angles under 40°. Samples subjected to plasma cleaning had improved contact angle results, with values under 5°. Doping the DLC films with SiO led to an average 40% decrease in modulus and 60% decrease in hardness. Hardness of the doped films, 12.0 - 13.2 GPa, was greater than that of the uncoated fused silica substrate, 9.2 GPa. The biocompatibility was assessed through CellTiter-Glo assays, with the films demonstrating statistically similar levels of cell viability when compared to the control media. The absence of ATP released by blood platelets in contact with the DLC coatings suggests in vivo hemocompatibility. The SiO doped films displayed improved transparency levels in comparison to undoped films, achieving up to an average of 80% transmission over the visible spectrum and an attenuation coefficient of 1.1 × 10(4) cm(-1) at the 450 nm wavelength. The SiO doped DLC films show promise as a method of fog prevention for laparoscopes.