Abstract
Over the past number of years, the power conversion efficiency of perovskite solar cells has remained at 25.5%, reflecting a respectable result for the general incorporation of organometallic trihalide perovskite solar cells. However, perovskite solar cells still suffer from long-term stability issues. Perovskite decomposes upon exposure to moisture, thermal, and UV-A light. Studies related to this context have remained ongoing. Recently, research was mainly conducted on the stability of perovskite against non-radiative recombination. This study improved a critical instability in perovskite solar cells arising from non-radiative recombination and UV-A light using a passivation layer. The passivation layer comprised a polyaniline (PANI) polymer as an interfacial modifier inserted between the active layer and the electron transport layer. Accordingly, the UV-A light did not reach the active layer and confined the Pb(2+) ions at PANI passivation layer. This study optimized the perovskite solar cells by controlling the concentration, thickness and drying conditions of the PANI passivation layer. As a result, the efficiency of the perovskite solar cell was achieved 15.1% and showed over 84% maintain in efficiency in the ambient air for one month using the 65 nm PANI passivation layer.