Abstract
This article shows the behavior of the corrosive effect of acid mine water on carbon steel metal alloys. Mining equipment, composed of various steel alloys, is particularly prone to damage from highly acidic water. This corrosion results in material thinning, brittle fractures, fatigue cracks, and ultimately, equipment failure. For this purpose, a set of carbon steel metal plates similar to those found in mine facilities were immersed into mine leachates of an AMD (Acid Mine Drainage) polluted river from the Tharsis Mine (Huelva, Spain). In these leachates, physicochemical variations occur, directly correlated with the alterations produced in the metal plates, manifested with the appearance of dissolved materials and particulate matter. Weight loss of up to 37 g in 30 weeks for plates of about 140 grs occurred and an increase in EC up to 45.64 mS/cm from 5.40 mS/cm and an increase in TDS from 2600 mg/L to 17,100 mg/L. STATGRAPHICS Centurion, a powerful data analysis tool was used for performing the time series analysis that was used for the first time to statistically define the corrosion effects on metal alloys. As a result, a significant variability in the physical and chemical factors of the leachates was observed due to the redox and precipitation-dissolution processes occurring within the system: an increase in total dissolved solids (TDS), electrical conductivity (EC) and temperature (T) (the corrosion process is an exothermic reaction) and a decrease in pH. It was also demonstrated that the longer the exposure time, the plates noticeably lost more material and became further weakened. Finally, these results allowed the formulation of a simple algorithm to define weight loss as a function of exposure time to acidic water.