Abstract
The impact of adding 1%, 3%, and 5% by mass of kaolin residue (KR) was investigated regarding the mechanical, thermomechanical, and morphological properties, as well as the non-isothermal crystallization and melting kinetics of poly(ε-caprolactone) (PCL). The processing to obtain the PCL/KR composites was carried out through extrusion in a twin-screw extruder, followed by injection molding. This study investigated the events of first melting, fusion crystallization, and second melting using differential scanning calorimetry (DSC), with heating rates ranging from 5 to 25 °C/min. Additionally, models for the expanded Prout-Tompkins equation (BNA), the nth-order reaction with m-power autocatalysis by product (Cnm), and the Sestak and Berggren equation (SB) were tested. The PCL/KR composites exhibited an increase in the elastic modulus and the heat deflection temperature (HDT) compared to the pure PCL. Furthermore, high ductility was observed, as evidenced by the impact strength and elongation at break. The good distribution of KR in the PCL matrix was confirmed by scanning electron microscopy (SEM), which contributed to a more efficient crystallization process. The increase in KR content in the PCL matrix shifted the crystallization sigmoids to higher temperatures, acting as a nucleating agent, which reduced the energy barriers and increased the crystallization temperature by up to 5 °C. The melting events did not show significant changes with the addition of the KR. The results are important for the plastics processing industry, mainly due to the opportunity to add value to the waste and use it as an additive.