Abstract
In this work, the effect of the palladium precursor on the Oxygen Reduction Reaction (ORR) performance of lignin-based electrospun carbon fibers was studied. The fibers were spun from a lignin-ethanol solution free of any binder, where different Pd salts were added at two concentration levels. The system implemented to perform the spinning was a coaxial setup in which the internal flow contains the precursor dispersion with the metallic precursor, and ethanol was used as external flow to help fiber formation and prevent drying before generating the Taylor cone. The obtained cloths were thermostabilized in air at 200 °C and carbonized in nitrogen at 900 °C. The resulting carbon fibers were characterized by physicochemical and electrochemical techniques. The palladium precursor significantly affects nanoparticle distribution and size, fiber diameter, pore distribution, surface area and electrochemical behavior. The fibers prepared with palladium acetylacetonate at high Pd loading and carbonized at 900 °C under a CO(2) atmosphere showed high mechanical stability and the best ORR activity, showing near total selectivity towards the 4-electron path. These features are comparable to those of the commercial Pt/C catalyst but much lower metal loading (10.6 wt.% vs. 20 wt.%). The most promising fibers have been evaluated as cathodes in a zinc-air battery, delivering astonishing stability results that surpassed the performance of commercial Pt/C materials in both charging and discharging processes.