This paper considers the uniaxial orientation effect on the structure and piezoelectric properties of vinylidene fluoride-tetrafluoroethylene copolymer ferroelectric films. The films were exposed to uniaxial orientation stretching in a temperature range from 20 °C to 60 °C; then, they were contact polarized under normal conditions. The temperature dependence of the electric strength was determined. The longitudinal piezoelectric coefficient d(33) values were measured by the quasi-static Berlincourt method. The piezoresponse force microscopy (PFM) method was used to investigate the film domain structure before and after polarization, and the local piezoelectric coefficient values were also calculated. Phase composition was studied using differential scanning calorimetry and infrared spectroscopy with the Fourier transform. It was found that uniaxial orientation stretching contributed to an increase in the piezoelectric coefficient d(33) from 5 pC/N to 16-20 pC/N. The results obtained indicate the importance of the amorphous phase contribution to the formation of the piezoelectric properties in polymeric materials.