Abstract
There has been an increase interest in natural plant fibers over the last decades with the intension to identify the ecologically acceptable alternatives to reduce the dependency on synthetic fibers. Naturally extracted okra fiber (Abelmoschus esculentus) was used in this study. Since okra is a stiff fiber, yarns with 100% Okra fiber was not possible to produce and tried to blend with polyester. The maximal ratio of okra was 20% with polyester to spin yarns in traditional ring spinning system. This study explores, for the first time, the possibility of manufacturing woven fabric with polyester-okra (80/20) yarns at weft direction with 100% cotton yarn at warp direction in order to prominent blend effect at weft direction. The properties of produced fabrics were compared with the same produced widely-used polyester-linen (PL) (80/20) counterpart. The both PO and PL woven fabrics were characterized in terms of fabric weight, thickness, abrasion, pilling, fuzzing, air permeability, tensile strength and tear strength. In addition, the morphological aspects of the fiber alignment in the woven fabric structure were observed using optical microscopic images. The performance of PO woven fabric was in acceptable ranges and can be considered as a sustainable blended woven fabric to meet the actual demand in the textile weaving industries.