Abstract
BACKGROUND: The objective of this study was to evaluate the impact of a single- vs. double-layer cementing technique on morphological cementation and the generation of microscopic cement layers or loose cement fragments in unicompartmental knee arthroplasty (UKA). METHODS: UKAs were implanted in 12 cadaver knees. The specimens were divided into two groups of comparable bone mineral density. Six UKAs were implanted using a single-layer cementing technique (group A) and six UKAs were implanted using a double-layer cementing technique (group B). Morphological cementation was assessed on nine cuts through the implant-cement-bone interface in the frontal plane. Loose bone cement fragments and the microscopically quality of layer formation were evaluated. RESULTS: Contact between bone and prosthesis was observed in 45.4% of interfaces in group A and 27.8% in group B (p = 0.126). The significant increase of areas without visible cement interlocking in the anteroposterior direction in group A (p = 0.005) was not evident in group B (p = 0.262). Penetration around the peg tended to occur more frequently in group B (67.5% vs. 90.6% p = 0.091). Scanning electron microscopy identified no evidence of fissure formations within the bilaminar cement mantle. Free bone cement fragments were documented in 66.7% in both groups with no difference concerning mass (p = 1.0). CONCLUSIONS: This in-vitro study showed a tendency towards a more homogenous cementation of tibial UKAs using a double-layer cementing technique, although most of the differences did not reach the level of significance. However, theoretical downsides of the double-layer cementing technique such as an increased formation of free bone fragments or a microscopically fissure formation within the cement layer could not be detected either.