Abstract
A novel Al-Cu-Zr alloy is designed in this paper, which provides a method for further improving the strength of Al-Cu alloys. In this paper, the addition of the micro-alloying element Zr in Al-Cu alloy was studied. The effect of aging treatment on the mechanical properties and precipitation behavior of the alloy was studied. With the addition of Zr, Al(3)Zr phases were formed in the alloy, which acts as obstacles to dislocation motion. In addition, Al(3)Zr phases can be used as the nucleation site of θ' phases to promote precipitation. All this can improve the strength of Al-Cu alloys. After one-step aging, corresponding to the highest hardness, the largest amount of θ' phases were observed in the alloy matrix. By contrast, after two-step aging, the θ' phases were finer, and a large amount of Guinier-Preston (GP) zones formed during the pre-aging step, which were transformed into denser and finer θ' phases in the secondary aging step. After the same solution treatment (540 °C/12 h), undergoing 120 °C/4 h + 175 °C/10 h two-step aging, the ultimate tensile strength, yield strength, and elongation of the Al-Cu-Zr alloy were 398.7 MPa, 313.3 MPa, and 7.9%, respectively.