Abstract
Although microcellular foams are potential thermal insulators, their low density and small pore size allow infrared radiation to pass through, increasing the effective thermal conductivity. To address this drawback, graphene nanoplatelets (GnPs) have previously been added to polymethylmethacrylate (PMMA) samples as infrared blockers, enhancing insulation by reducing the radiative component of heat transfer. In this work, the effect of the content of GnPs is studied. Cellular PMMA samples with GnP contents ranging from 0.5 to 10 weight total percentage (wt. %) and pore sizes between 2 and 5 microns were tested. Thermal conductivity measurements showed that GnP additions from 0.5 to 5 wt. % significantly decrease the radiative term, achieving a 33% reduction compared to pure PMMA and reaching thermal conductivity values of 38 mW m(-1) K(-1). Moreover, the structural factor is diminished up to 45% in comparison to pure microcellular PMMA, which, in samples with contents of GnPs such as 1 wt. %, results in a reduction in the conductivity of the solid phase. This approach demonstrates that incorporating small contents of GnPs effectively enhances the thermal performance of microcellular foams, a strategy that could be applied to other polymers to achieve better thermal insulation properties.