Abstract
Zinc cobalt oxide-zinc hydroxide (ZnCo2O4-Zn(OH)2) microspheres were successfully fabricated on carbon cloth via a sample hydrothermal method. The surface morphology of these microspheres and their efficacy in degrading methyl violet were further modulated by varying the thermal annealing temperatures. Adjusting the thermal annealing temperatures was crucial for controlling the porosity of the ZnCo&sub2;O&sub4;-Zn(OH)&sub2; microspheres, enhancing their photocatalytic performance. Various analytical techniques were utilized to evaluate the physical and chemical properties of the ZnCo2O4-Zn(OH)2 microspheres, including field-emission scanning electron microscopy, energy-dispersive spectroscopy, X-ray diffraction, field-emission transmission electron microscopy, X-ray photoelectron spectroscopy, and UV-vis spectroscopy. Compared to untreated ZnCo2O4-Zn(OH)2 microspheres, those subjected to thermal annealing exhibited increased specific surface area and light absorption capacity, rendering them highly effective photocatalysts under UVC light exposure. Subsequent studies have confirmed the superior performance of ZnCo2O4-Zn(OH)2 microspheres as a reusable photocatalyst for degrading methyl violet and tetracycline. Furthermore, trapping experiments during the photodegradation process using ZnCo&sub2;O&sub4;-Zn(OH)&sub2; microspheres identified hydroxyl radicals (·OH) and superoxide radicals (·O&sub2;⁻) as the primary reactive species.