Abstract
To construct a complex three-dimensional (3D) structure mimicking bone microstructure, hydrogel models of polymerized gelatin methacrylate (pGelMA) were fabricated by using stereolithography and modified with hydroxyapatite (HAp) via an alternate soaking process (ASP) using a solution of calcium and phosphate ions. Fabricated pGelMA line models whose widths were designed as 100, 300, and 600 μm were modified with HAp by ASP by changing the immersion time and number of cycles. After ASP, all of the line models with widths of 100, 300, and 600 μm were successfully modified with HAp, and large amounts of HAp were covered with the fabricated models by increasing both the immersion time and the number of cycles in ASP. HAp was observed near the surface of the line model with a width of 600 μm after ASP at an immersion time of 10 s, while the entire model was modified with HAp using ASPs for longer immersion times. The adhesion and spread of mesenchymal stem cells (MSCs) on the pGelMA-HAp discs depended on the ASP conditions. Moreover, the HAp modification of 3D pyramid models without alteration of the microstructure was also conducted. This two-step fabrication method of first fabricating frameworks of hydrogel models by stereolithography and subsequently modifying the fabricated models with HAp will lead to the development of 3D cell culture systems to support bone grafts or to create biological niches, such as artificial bone marrow.